Solidification Structures

Macrostructure of a VIM (vacuum induction melted) ingot of Fe-52% Ni alloy. A slice was cut transverse to the ingot axis and hot acid etched (50% HCl at 70 °C) revealing the solidification pattern. There is a very thin surface zone of small grains. Below the surface, there is a zone of columnar grains and the central portion is equiaxed but coarse. The scale is in inches.

Transverse Concast Discs, 430 SS

Macrostructure of 5-inch square (127 mm) continuously cast billets of type 430 stainless steel (Fe - 0.03% C – 0.34% Mn – 0.48% Si – 17.78% Cr – 0.26% Ni – 0.05% Mo – 0.07% Cu) taken at three random locations along the strand. The discs were cut transverse to the growth direction and were hot acid etched. Note the thin region of fine grains at the surface, the large columnar zone and the central equiaxed zone (of varying coarseness). Note that there are some fine cracks present.

DOWNLOAD THE PRESENTATION HERE

resourcesThe articles and presentations that can be down-loaded from this web site are based upon work done by GFV while employed at Bethlehem Steel (1967-1983), Carpenter Technology (1983-1996), Buehler Ltd. (1996-2009) and Struers (2009-Present) and from the authors consulting work for companies such as, Latrobe Steel, Scot Forge, etc., and from his litigation work. GFV's bylined articles appearing in various issues of the ASM Handbook series have been listed here courtesy of ASM International, Materials Park, Ohio.

Log in to your account or